How do you obtain the wrought iron?

Wrought iron, one of the two forms in which iron is obtained by smelting; the other is cast iron (q.v.). Wrought iron is a soft, ductile, fibrous variety that is produced from a semifused mass of relatively pure iron globules partially surrounded by slag.

Can you make wrought iron?

Modern wrought iron is made from 1018 mild steel rather than the low-to-no-carbon iron of the past, due to cost. “Wrought” means worked by hand. The methods used to produce the rails, supports and scrollwork seen in true wrought iron take time and practice to perfect.

How long do wrought iron railings last?

Once you treat your wrought iron railings and fences with proper sealing and maintenance, you can expect them to last a minimum of 60 years, though often they last more than a lifetime, especially as it comes to indoor railings.

Who is the real wrought iron company UK?

The Real Wrought Iron Company is a UK firm which restores historic ironwork and supplies wrought iron, puddled (post-1800) and charcoal (pre-1800). For more information please email: Copyright © 2020 TWI Ltd. All rights reserved. Copyright © 2020 TWI Ltd. All rights reserved. Terms Privacy Cookies Modern Slavery Statement Safeguarding Policy

Who is the company that restores Wrought iron?

Chris Topp & Co Ltd 01845 501415, reclamation of wrought iron. The Real Wrought Iron Company is a UK firm which restores historic ironwork and supplies wrought iron, puddled (post-1800) and charcoal (pre-1800).

Where can I find examples of wrought iron?

Notable examples are the Palm House at Kew Gardens, restored under the direction of Posford Pavry and Partners, and the G-MEX Exhibition Centre in Manchester. Originally, wrought-iron structures were either bolted or riveted and, in addition to general corrosion, more serious rusting is often found in the region of the connections.

What is the procedure for welding wrought iron?

The procedure for welding wrought iron is, in general, the same as that used for welding structural steel. However, excessive penetration into the parent plate should be avoided to reduce the risk of slag inclusions in the weld metal.